Ultra Low Temperature Electrophoretic Coating Anti Corrosion Coating For Car

Solution for the Car shock electrophoresis paint.

Product Introduction

OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating, such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable

This product features shown below: 

Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material.

Ultra low temperature curing completely green does not contain heavy metals, in conformity with the European ROHS, the instruction of PAHs, reach, fohs, can save about 60% of the energy consumption, is the national government absolute attention and support energy-saving emission reduction requirements of the project, the state and the enterprises and the people.

Main ingredients

Additives: surface active agent, prevent shrinkage cavity agent

Pigment: carbon black, kaolin, antirust pigment

Solvent: alcohol ether

Product quality data

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

Filling tank proportion and method

⑴ Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(130-140)℃×(20-30)min (Keeping temperature of parts coated)

Product film performance

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

Construction equipment

Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment: 

Electrophoresis tank 

Circulation devices (including filter, fill the paint device) 

DI water equipment 

DC power supply and the power supply unit 

Anode box (tube) and circulation device 

Ultrafiltration device 

Cleaning devices 

Heat exchanging equipment 

Curing device

Customers in the electric vehicle industry